G80 Alloy Steel High Tensile Welding Lifting Hoist Chain for Overloading Industry
G80 Alloy Steel High Tensile Welding Lifting Hoist Chain for Overloading Industry
Ẹka
Gbigbe ati fifẹ, pq, ọna asopọ kukuru kukuru, gbigbe ọna asopọ ọna asopọ yika, Iwọn 80 pq, pq G80, sling pq, awọn ẹwọn sling, DIN 818-2 pq ifarada alabọde fun awọn slings pq ite 8, alloy, steel pq
Ohun elo
Gbigbe ati fifin, awọn ẹru gbigbe, awọn ẹru abuda
Awọn ẹwọn SCIC Grade 80 (G80) fun gbigbe ni a ṣe gẹgẹbi fun awọn iṣedede EN 818-2, pẹlu nickel chromium molybdenum manganese alloy steel fun awọn ajohunše DIN 17115; ti a ṣe apẹrẹ daradara / abojuto alurinmorin & itọju ooru ṣe idaniloju awọn ẹwọn awọn ohun-ini ẹrọ pẹlu agbara idanwo, agbara fifọ, elongation & líle.
Nọmba 1: Awọn iwọn ọna asopọ pq 80 ite
Table 1: Ite 80 (G80) pq mefa, EN 818-2
| opin | ipolowo | igboro | àdánù kuro | |||
| ipinfunni | ifarada | p (mm) | ifarada | inu W1 | ode W2 | |
| 6 | ± 0.24 | 18 | ± 0.5 | 7.8 | 22.2 | 0.8 |
| 7 | ± 0.28 | 21 | ± 0.6 | 9.1 | 25.9 | 1.1 |
| 8 | ± 0.32 | 24 | ± 0.7 | 10.4 | 29.6 | 1.4 |
| 10 | ± 0.4 | 30 | ± 0.9 | 13 | 37 | 2.2 |
| 13 | ± 0,52 | 39 | ± 1.2 | 16.9 | 48.1 | 4.1 |
| 16 | ± 0.64 | 48 | ± 1.4 | 20.8 | 59.2 | 6.2 |
| 18 | ± 0.9 | 54 | ± 1.6 | 23.4 | 66.6 | 8 |
| 19 | ± 1 | 57 | ± 1.7 | 24.7 | 70.3 | 9 |
| 20 | ± 1 | 60 | ± 1.8 | 26 | 74 | 9.9 |
| 22 | ± 1.1 | 66 | ± 2.0 | 28.6 | 81.4 | 12 |
| 23 | ± 1.2 | 69 | ± 2.1 | 29.9 | 85.1 | 13.1 |
| 24 | ± 1.2 | 72 | ± 2.1 | 30 | 84 | 14.5 |
| 25 | ± 1.3 | 75 | ± 2.2 | 32.5 | 92.5 | 15.6 |
| 26 | ± 1.3 | 78 | ± 2.3 | 33.8 | 96.2 | 16.8 |
| 28 | ± 1.4 | 84 | ± 2.5 | 36.4 | 104 | 19.5 |
| 30 | ± 1.5 | 90 | ± 2.7 | 37.5 | 105 | 22.1 |
| 32 | ± 1.6 | 96 | ± 2.9 | 41.6 | 118 | 25.4 |
| 36 | ± 1.8 | 108 | ± 3.2 | 46.8 | 133 | 32.1 |
| 38 | ± 1.9 | 114 | ± 3.4 | 49.4 | 140.6 | 35.8 |
| 40 | ± 2 | 120 | ± 4.0 | 52 | 148 | 39.7 |
| 45 | ± 2.3 | 135 | ± 4.0 | 58.5 | 167 | 52.2 |
| 48 | ± 2.4 | 144 | ± 4.3 | 62.4 | 177.6 | 57.2 |
| 50 | ± 2.6 | 150 | ± 4.5 | 65 | 185 | 62 |
Table 2: ite 80 (G80) pq darí ini, EN 818-2
| opin | ṣiṣẹ fifuye iye to | agbara ẹri iṣelọpọ | min. fifọ agbara |
| 6 | 1.12 | 28.3 | 45.2 |
| 7 | 1.5 | 38.5 | 61.6 |
| 8 | 2 | 50.3 | 80.4 |
| 10 | 3.15 | 78.5 | 126 |
| 13 | 5.3 | 133 | 212 |
| 16 | 8 | 201 | 322 |
| 18 | 10 | 254 | 407 |
| 19 | 11.2 | 284 | 454 |
| 20 | 12.5 | 314 | 503 |
| 22 | 15 | 380 | 608 |
| 23 | 16 | 415 | 665 |
| 24 | 18 | 452 | 723 |
| 25 | 20 | 491 | 785 |
| 26 | 21.2 | 531 | 850 |
| 28 | 25 | 616 | 985 |
| 30 | 28 | 706 | 1130 |
| 32 | 31.5 | 804 | 1290 |
| 36 | 40 | 1020 | Ọdun 1630 |
| 38 | 45 | 1130 | 1810 |
| 40 | 50 | 1260 | Ọdun 2010 |
| 45 | 63 | 1590 | 2540 |
| 48 | 72 | 1800 | 2890 |
| 50 | 78.5 | Ọdun 1963 | 3140 |
| awọn akọsilẹ: lapapọ Gbẹhin elongation ni fi opin si agbara ni min. 20%; | |||
| awọn iyipada ti Ifilelẹ fifuye Ṣiṣẹ ṣiṣẹ ni ibatan si iwọn otutu | |
| Iwọn otutu (°C) | WLL% |
| -40 si 200 | 100% |
| 200 si 300 | 90% |
| 300 si 400 | 75% |
| ju 400 lọ | itẹwẹgba |